Ti-6Al-4V
grade 5
Titanium alloy
Ti-6Al-4V grade 5
Ti-6Al-4V grade 5 is ideal for application needing a higher strength, lower ductility compared to grade 23 across medial and aerospace industries.
Particle size distribution
0-20 µm
15-45 µm
45-106µm
45-150µm
Typical values
PSD
Size distribution by laser diffraction (ASTM B822)
Apparent density (ASTM B212)
Flow rate (ASTM B213)
Oxygen content
Application Technology
D10
D50
D90
0-20 µm
6 µm
13 µm
19 µm
2.8
g/cm 3*
g/cm 3*
-
0.19 w%
MIM
15-45 µm
20 µm
34 µm
44 µm
2.49
g/cm 3
g/cm 3
28 s
0.16 w%
L-PBF
15-53 µm
22 µm
39 µm
54 µm
2.52
g/cm 3
g/cm 3
28 s
0.16 w%
L-PBF
20-63 µm
26 µm
46 µm
60 µm
2.57
g/cm 3
g/cm 3
28 s
0.15 w%
L-PBF
15-106 µm
27 µm
54 µm
88 µm
2.61
g/cm 3
g/cm 3
25 s
0.13 w%
L-PBF
45-106 µm
52 µm
71 µm
102 µm
2.47
g/cm 3
g/cm 3
25 s
0.13 w%
EB-PBF, L-PBF, DED
45-150 µm
54 µm
86 µm
142 µm
2.59
g/cm 3
g/cm 3
25 s
0.13 w%
DED
*Tap density as per ASTM B527
Various particle sizes are available upon request
Ti-6Al-4V grade 5 offers outstanding biocompatibility, making it perfect for medical implants. Its superior corrosion resistance ensures longevity and reliability in demanding environments. This alloy is widely used in the aerospace industry for critical components, in the medical field for durable implants, and in high-performance motorsports for lightweight, robust parts. Its versatile properties make Ti6Al4V Grade 5 a preferred choice across these advanced industries.